| Place of Origin: | CHINA |
| اسم العلامة التجارية: | UPCERA |
| إصدار الشهادات: | CE、 FDA 、CFDA、KFDA |
| Model Number: | HT-White |
| الأسعار: | Negotiation |
|---|---|
| Packaging Details: | Carton |
| Delivery Time: | 10 working days after received your payment |
| Payment Terms: | T/T |
| Density before sintering (g/cm3): | 3.1±0.5 g/cm3 | Density after sintering (g/cm3): | 6.07±0.01 g/cm3 |
|---|---|---|---|
| CTE after sintering (25-200℃): | (10.5±1.0)x10-6K-1 | 3-point bending strength after sintering (MPa): | 1400Mpa |
| Average transmittance (1.0±0.02mm): | 37% | Chemical solubility after sintering (μg/cm2): | < 100 |
| Radioactivity after sintering (Bq/g): | <0.1 | Sintering temperature (℃): | 1450-1550℃Recommended 1530℃ |
| تسليط الضوء: | zirconium dioxide ceramic, dental ceramic materials,dental ceramic materials |
||
HT White Blank Yttria Stabilized Zirconia Ceramic for Wieland System
Zirconia blocksare made of nanometer medical grade zirconia powder. The powder are firstly compacted by cold isostaticpressing with high compressive strength and then pre-sintered to a certain degree to offer good machinability.
Our zirconia blocks can be used to create crowns, bridges, inlays and veneers of fixed partial denture with different translucency levels and colors.
These blanks are distinguished by their enhanced strength and long-term hydrothermal stability. An absolutely homogenous structure is achieved through a specially developed production process. The blanks are optimised for rapid milling strategies and provide excellent edge stability and green body breaking strength during processing.
Indications
|
|
HT white |
|
Framework |
√ |
|
3-4 units Framework |
√ |
|
5-6 units Framework |
√ |
|
Bridges over 7 units |
√ |
|
Cantilever bridge |
√ |
|
Inlay bridge |
√ |
|
Maryland bridge |
√ |
|
Telescopic crown |
√ |
|
Personalized abutment |
√ |
Specifications
|
Wieland System |
|
D98*10 |
|
D98*12 |
|
D98*14 |
|
D98*16 |
|
D98*18 |
|
D98*20 |
|
D98*22 |
|
D98*25 |
Zirconia blocks are made of nanometer medical grade zirconia powder. The powder are firstly compacted by cold isostatic pressing with high compressive strength and then pre-sintered to a certain degree to offer good machinability.
Upcera zirconia blocks can be used to create crowns, bridges, inlays and veneers of fixed partial denture with different translucency levels and colors.
Our company
1. Leading Manufacturer for 10 years with advanced facilities
2. Strict Quality Control: CE & ISO9001:2000 Approved
3. Cooperate with many famous companies in Europe and USA
4. Professional Research & development department
5. A high standard of product knowledge and customer service
Our service
1. Factory prices with the best quality.
2. One year free-of-charge maintenance for all the dental equipment
3. Customized service for special demand
4. Fast and flexible delivery, by sea, by air, by express
5. Quick response within 24 hours
Extra Service
1. Sample order is available.
2. Offer Customized service
اتصل شخص: sales
الهاتف :: +8613438862501
متعدد الطبقات زركونيا الأسنان كتل CE ISO FDA مصدق زركونيا مواد طب الأسنان
معدات طب الأسنان مستلزمات طب الأسنان Zirconia CAD CAM فارغة TT أبيض 49٪ شفاف
Cerec Zirconia Blocks Manul Milling System Compatible For Zirconium Dental Crowns
Cerec Zirconia Block 98 × 12 mm منخفض المشعة للتجار الخزف
ST White Blank High Translucent Zirconia Dental لنظام مفتوح 16 ظلال
كتل زركونيا الأسنان فارغة عالية شفافة لنظام CAD / CAM المفتوح
Pre Sintered Dental Zirconia Blank St Multilayer For Sirona System
Super Transparent Dental Zirconia Blank 16 Colors Without Coloring Liqiuids